Designation: D – 11Standard Test Methods for Field Measurement of Surface These test methods are under the jurisdiction of ASTM Committee D01 on. There are two ASTM standards that deal with surface profile assessment, D , Standard Test. Methods for Field Measurement of Surface Profile of Blast. 18 Oct For hot-dip galvanizing applications, it is possible to measure and verify the steel surface profile according to ASTM D, Standard Test.

Author: Vobei Madal
Country: Barbados
Language: English (Spanish)
Genre: Education
Published (Last): 16 June 2007
Pages: 139
PDF File Size: 11.40 Mb
ePub File Size: 11.10 Mb
ISBN: 500-5-21356-157-3
Downloads: 65735
Price: Free* [*Free Regsitration Required]
Uploader: Gojar

Recent changes to ASTM D provide updated test methods to reflect the latest advances in technology and ast accepted industry research. Profile depth designations are based on the concept of mean maximum profile h max ; this value is determined by averaging a given number usually astm d 4417 of the highest peak to astm d 4417 valley measurements made in the field of view of a standard measuring microscope.

Link to Active This link will always route to the current Active version of the standard. While both the depth micrometer and replica tape asstm conform to ASTM D, the measurement acquisition principles are quite different.

How is Surface Asgm Depth Quantified? So, in effect the reading on the micrometer astj the RTR from astm d 4417 replica tape represents several peaks and valleys, while the depth micrometer does not. Standards for Measurement of Surface Profile There are currently four primary standards for measurement of surface profile in steel surfaces.

The depth is displayed on the gage in mils 0. Larger repair areas or prepared hot-dip galvanized astm d 4417 for painting can be measured with 10 readings taken from a minimum of three, 6×6 inch astm d 4417 cm areas. Work Item s – proposed revisions of this standard. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. This movement may be caused by expansion and contraction of the substrate due to temperature fluctuation, or live loads placed onto a structure; for example, traffic crossing a bridge.

Standards for Measurement of V Profile. Save my name, email, and website in this 44417 for the next time I comment. According to ASTM D, a minimum of 10 readings is obtained per area; the maximum surface astm d 4417 is reported discarding obvious outliers.

It is the astm d 4417 of whoever uses this standard to consult and establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Today, Method B and Method C are the most commonly used, so that is what we will be focusing on. For measurements adtm fall between tape sizes, it is still required that two readings using each tape astm d 4417 44117 be averaged to comprise one reading i.

The standard does not address discarding outliers, but an update to the standard addressing outlier readings is planned. Note 1 — Optical microscope methods serve as a referee method for surface profile measurement methods A and B.

Updates to ASTM D | American Galvanizer’s Association

The three test methods described within D for measuring surface profile include visual comparators, surface profile depth micrometers, and replica tape. Your email address will not be published. This method can be used to measure the surface profile depth that is created by abrasive blast cleaning or impact-type power tools. Instead, recording of the astm d 4417 reading 4417 using a depth micrometer most closely astm d 4417 the same measurements produced asmt replica tape.

For this reason, surface profile should be measured prior to coating application to ensure that it meets that specified. Same Surface, Different Results?

There are additional techniques suitable for astm d 4417 use not covered by these test methods. This includes personalizing content and advertising. Historical Version s – view previous versions of standard. The creation of this peak-valley pattern astm d 4417 the surface effectively increases the surface area, providing an anchor for the coating system. Larger repair areas or prepared hot-dip galvanized surfaces for painting can be measured with two readings taken from a minimum of three, 6×6 inch 15×15 cm areas.

The astm d 4417 standards are: These changes reflect industry research on current tooling which revealed averaged 44117 are consistently less than the values obtained using replica tape. During abrasive blast cleaning, the mass of the abrasive and the velocity of the abrasive movement created by compressed air generates kinetic energy the abrasive can reach speeds of over miles per hour as it exits the blast nozzle.

Peak density the number of peaks per unit area also plays a key role in maintaining astm d 4417 of the coating awtm and provides greater resistance to corrosion undercutting when the astm d 4417 system gets damaged while in qstm.

By continuing to use our site, you accept our use of cookies To learn more, click Read More to view our Privacy and Cookies Policy.

Authored by Alana Hochstein. Once the burnishing process is complete, the replica tape is removed from the surface and the image is measured using astm d 4417 spring-loaded micrometer. The instruments described are readily astm d 4417 and sufficiently sturdy for use in the field. Replica Tape – Although the technology has remained mostly constant for replica tape since its introduction, industry zstm has addressed the sufficient number of readings required to achieve an accurate measurement.

Historical Version astm d 4417 – view previous versions of standard Work Item s – proposed revisions of this standard Translated Version s: Typically, the higher the coating thickness the greater the surface profile depth. The values given in parentheses are for information only. Only the use of surface profile depth micrometers and replica tape were updated, and the specification changes are as follows: The surface profile must be compatible with the coating system.

Visual Comparator – This test method, as well as the comparator discs available on the market, have stayed the same, and therefore there were no updates for aastm test method.

ASTM D4417 – 14

Only the use of surface profile depth micrometers and replica tape astm d 4417 updated, and the specification changes are as follows:. What is Surface Profile and Why is it Necessary? We use astm d 4417 to understand how you use our site and to improve your experience. Models from a few gage manufacturers are available that conform to this standard. According to ASTM D, a minimum of 2 readings is obtained per area; the average of the two readings is reported.

October 18, Aastm by Alana Hochstein. When the abrasive impacts the surface, it cuts into the surface angular abrasives or peens the surface round abrasives and 4471 a series of peaks and astm d 4417 in the surface. Surface profile is defined as a measurement of the maximum peak-to-valley depth created astm d 4417 abrasive impingement against a surface during abrasive blast cleaning operations, or by an impact-type power tool. This is done because of evidence that coatings performance in any one small area is primarily influenced by the highest surface features in that area and not by the average roughness.